Synthesis, Magnetic, and Photocatalytic Activity of Polypyrrole-Based TiO2–Fe Catalyst for Wastewater Treatment
Author
Other authors
Publication date
2024-10-05ISSN
2073-4344
Abstract
The primary aim of this study is to investigate the degradation efficacy of the Ppy/TiO2-Fe photocatalyst for MB dye in an aqueous solution. Firstly, the direct addition of TiO2 and Fe was done to prepare Ppy/TiO2-Fe photocatalyst. Fourier transformation infrared spectroscopy, XRD, SEM, BET surface area analysis, and magnetization tests established the formation of the Ppy/TiO2-Fe photocatalyst. The crystallite sizes of TiO2, Fe-TiO2, and Ppy/TiO2-Fe photocatalyst were estimated to be 24.99 nm, 21.94 nm, and 21.84 nm, respectively. For the synthesis confirmation, the FTIR spectrum confirmed the existence of Ti-O, Fe-O, and Ppy-related bonds. While comparing the SEM images, the impact of polypyrrole on the particle shape was observed with less aggregation and increased surface roughness. The VSM analysis revealed that incorporating polypyrrole (Ppy) into Fe-TiO2 significantly enhances its magnetic properties, with Ppy/TiO2-Fe exhibiting superparamagnetic behavior, characterized by a higher saturation magnetization (Ms) of 33.11 emu/g and a lower coercivity (Hc) of 0.160 Oe, compared to Fe-TiO2’s Ms of 1.09 emu/g and Hc of 341.39 Oe. The N2 sorption desorption, with a specific surface area of 2.25 × 102 m2/g, is beneficial for photocatalytic activity. The concentration of dye, amount of catalyst, pH, and temperature were studied to evaluate the photocatalytic efficiency of the synthesized Ppy/TiO2-Fe photocatalyst under different conditions. The findings revealed a degradation efficiency of 91.92%. The degradation rate reached 91.92% under optimal conditions within 120 min and could be fitted well by first-order kinetics. The photocatalytic efficiency was also evaluated for the scavenger, and the concentration of H2O2 and the reusability of the catalyst were demonstrated. Based on the observed results, the Ppy/TiO2-Fe photocatalyst could be applied more effectively and efficiently to photocatalytic degradation of organic dyes in wastewater treatment.
Document Type
Article
Document version
Published version
Language
English
Subject (CDU)
544 - Physical chemistry
Keywords
polymer
dye degradation
water treatment
photocatalyst
magnetism
Pages
22 p.
Publisher
MDPI
Is part of
Catalysts. 2024;14(10):692
This item appears in the following Collection(s)
Rights
© L'autor/a
Except where otherwise noted, this item's license is described as http://creativecommons.org/licenses/by/4.0/